gear
Powder preparation method: electrolysis
Molding method: Compression molding
Mold material: Carbide mold
Mold Type: Compression Mold
Sintering method: Ammonia furnace
Sintering atmosphere: decomposed ammonia
Sintering temperature: 1050-2000
Compression method: bidirectional molding
Post-processing: According to customer's requirements
Proofing cycle: 16 days or more
Processing period: 16 days or more
Annual processing capacity: 500000
Annual surplus processing capacity: 500000
Material: Iron-based
Product Type: Gear
Powder pretreatment: Mixing